The influence of inorganic elements on lignin ‐based carbon fibre (CF) quality was studied using sulphates of Na +, K+, Mg2+, Fe2+, Al3+. The metal sulphates were added to wet spun prefibres made from softwood kraft lignin (SKL):cellulose (70:30) and melt spun prefibres made from low molecular mass SKL. An increase in concentration from 0.1 w% to about 0.4 w% did neither affect the mechanical properties nor the morphology as observed by SEM. In contrast, metal sulphates added to the initial 0.45 w% to a total range 1.5 to 5.0 w%, was found detrimental to the melt spinning and to the final CF quality. Thus, the recommendation of <0.1 w% ash in kraft lignin may be exceeded, but more research is needed to establish the upper concentration limit.