Objective To adequately address clinically important issues such as osseointegration and soft tissue integration, we screened for the direct biological cell response by culturing human osteoblasts and gingival fibroblasts on novel zirconia-based dental implant biomaterials and subjecting them to transcriptional analysis. Methods Biomaterials used for osteoblasts involved micro-roughened surfaces made of a new type of ceria-stabilized zirconia composite with two different topographies, zirconium dioxide, and yttria-stabilized zirconia (control). For fibroblasts smooth ceria- and yttria-stabilized zirconia surface were used. The expression of 90 issue-relevant genes was determined on mRNA transcription level by real-time PCR Array technology after growth periods of 1 and 7 days. Results Generally, modulation of gene transcription exhibited a dual dependence, first by time and second by the biomaterial, whereas biomaterial-triggered changes were predominantly caused by the biomaterialsâ chemistry rather than surface topography. Per se, modulated genes assigned to regenerative tissue processes such as fracture healing and wound healing and in detail included colony stimulating factors (CSF2 and CSF3), growth factors, which regulate bone matrix properties (e.g. BMP3 and TGFB1), osteogenic BMPs (BMP2/4/6/7) and transcription factors (RUNX2 and SP7), matrix collagens and osteocalcin, laminins as well as integrin Ã1 and MMP-2. Significance With respect to the biomaterials under study, the screening showed that a new zirconia-based composite stabilized with ceria may be promising to provide clinically desired periodontal tissue integration. Moreover, by detecting biomarkers modulated in a time- and/or biomaterial-dependent manner, we identified candidate genes for the targeted analysis of cell-implant bioresponse during biomaterial research and development.
Objectives. The aim of this study was to evaluate the bone tissue response to fiber-reinforced composite (FRC) in comparison with titanium (Ti) implants after 12 weeks of implantation in cancellous bone using histomorphometric and ultrastructural analysis. Materials and methods. Thirty grit-blasted cylindrical FRC implants with BisGMA-TEGDMA polymer matrix were fabricated and divided into three groups: (1) 60 s light-cured FRC (FRC-L group), (2) 24 h polymerized FRC (FRC group), and (3) bioactive glass FRC (FRC-BAG group). Titanium implants were used as a control group. The surface analyses were performed with scanning electron microscopy and 3D SEM. The bone-implant contact (BIC) and bone area (BA) were determined using histomorphometry and SEM. Transmission electron microscopy (TEM) was performed on Focused Ion Beam prepared samples of the intact bone-implant interface. Results. The FRC, FRC-BAG and Ti implants were integrated into host bone. In contrast, FRC-L implants had a consistent fibrous capsule around the circumference of the entire implant separating the implant from direct bone contact. The highest values of BIC were obtained with FRC-BAG (58 ± 11%) and Ti implants (54 ± 13%), followed by FRC implants (48 ± 10%), but no significant differences in BIC or BA were observed (p = 0.07, p = 0.06, respectively). TEM images showed a direct contact between nanocrystalline hydroxyapatite of bone andboth FRC and FRC-BAG surfaces. Conclusion. Fiber-reinforced composite implants are capable of establishing a close bone contact comparable with the osseointegration of titanium implants having similar surface roughness.
Objectives: Surface characteristics of implant reconstructions determine the gingival fibroblast (GF) response and thus soft tissue integration (STI). However, for monolithic implant reconstructions it is unknown whether the (hybrid) ceramic biomaterial type and its surface treatment affect GF response. Therefore, this investigation examined the influence of the implant reconstruction biomaterials hybrid ceramic (HC), lithium disilicate ceramic (LS), 4 and 5 mol% yttria partially stabilized zirconiumdioxide ceramics (4/5Y-PSZ) and their surface treatment - machining, polishing or glazing - on surface characteristics and GF response. Methods: After characterization of surface topography and wettability by scanning electron microscopy, interferometry and contact angle measurement, the adhesion, morphology, metabolic activity and proliferation of GFs from six donors was investigated by fluorescent staining and a resazurin-based assay at days 1, 3 and 7. Titanium (Ti) served as control. Results: Biomaterial type and surface treatment affected the GF response in a topography-dependent manner. Smooth polished and glazed surfaces demonstrated enhanced GF adhesion and earlier proliferation onset compared to rough machined surfaces. Due to minor differences in surface topography of polished and glazed surfaces, however, the GF response was similar for polished and glazed HC, LS, 4- and 5Y-PSZ as well as Ti. Significance: Within the limits of the present investigation, polishing and glazing of machined HC, LS and 4/5Y-PSZ can be recommended to support STI-relevant cell functions in GF. Since the GF response on polished and glazed HC, LS, 4- and 5Y-PSZ surfaces and the Ti control was comparable, this investigation proofed equal cytocompatibility of these surfaces in vitro. © 2024 The Authors
OBJECTIVE: To investigate the long-term stability of a metal-free zirconia two-piece implant assembled with a carbon fiber-reinforced (CRF) screw by means of transformation propagation, potential changes in surface roughness, the gap size of the implant-abutment connection, and fracture load values.
METHODS: In a combined procedure, two-piece implants made from alumina-toughened zirconia were dynamically loaded (107 cycles) and hydrothermally aged (85°, 60days). Implants made from titanium (Ti) and a titanium-zirconium (TiZr) alloy with a titanium abutment screw served as control. Transformation propagation (ATZ) and gap size of the IAC were monitored at cross-sections by scanning electron microscopy (SEM). Furthermore, changes in surface roughness of ATZ implants were measured. Finally, implants were statically loaded to fracture. Linear regression models and pairwise comparisons were used for statistical analyses.
RESULTS: Independent of the implant bulk material, dynamic loading/hydrothermal aging did not decrease fracture resistance (p=0.704). All test and control implants fractured at mean loads >1100N. Gap size of the IAC remained stable (<5μm) or decreased. None of the CFR screws fractured during static or dynamic loading. Monoclinic layer thickness of ATZ implants increased by 2-3μm at surfaces exposed to water, including internal surfaces of the IAC. No changes in surface roughness were observed.
SIGNIFICANCE: Combined hydrothermal aging and dynamic loading did not affect the above-mentioned parameters of the evaluated two-piece ATZ implant. Mean fracture loads >1100N suggest a reliable clinical application.
Objectives: The aim of this study was to investigate the effect of photosensitive initiator and activator concentrations on the degree of conversion and flexural properties of an experimental photopolymerized dental copolymer containing dendrimer. Methods: The experimental resin system consisted of a dendrimer with 12 methacrylate groups and methyl methacrylate in a mass ratio of 80:20. The initiator and activator used were camphorquinone and 2-(N,N-dimethylamino)ethyl methacrylate, whose concentrations varied individually from 1 to 4wt%. The degree of conversion was determined with FTIR spectroscopy, and flexural strength and flexural modulus with the three-point bending test. The experiments were designed and analyzed, and the results plotted with Modde 5.0 software. Results: The highest degree of conversion was obtained with 2.5wt% initiator and activator concentrations, the highest flexural strength with 2.5wt% initiator and 1.0wt% activator concentration, and the highest flexural modulus with 1.0wt% initiator and activator concentrations. Significance: The results indicated that the degree of conversion increased, and flexural strength and flexural modulus decreased, with increasing initiator and activator concentrations. The high concentrations of initiator probably inhibited the transmittance of the active wavelengths to the depths of the samples (the inner filter effect), resulting in inhomogeneous conversion and thus decreased mechanical properties. © 2004 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.