The determination properties of nine commercial multiply board grades, both coated and uncoated, were measured using four testing methods, the Z-Directional Tensile Strength test (ZDTS), the Scott Bond Test (SBT), the Wheel Delamination Test (WDT), and the IGT method. The positions of delamination failure in the thickness direction were then recorded and compared. For the IGT tests, failure profiles and the final failure positions were evaluated. The results showed that the failures in the ZDTS, WDT and SBT tests mainly occur in the middle ply, whereas failure in the IGT tests occurs in the top plies as well as in the middle ply. Some boards presented also more than one failure position for the same type of test. The correlations between the different delamination resistances were also investigated. The WDT and SBT method showed a good correlation, whereas no correlation could be found between the other methods.