Effect of cations on corrosion of zinc and carbon steel covered with chloride deposits under atmospheric conditions 2007 (engelsk)Inngår i: Corrosion Science, ISSN 0010-938X, E-ISSN 1879-0496, Vol. 49, nr 6, s. 2676-2693Artikkel i tidsskrift (Fagfellevurdert) Published

Abstract [en]

The effect of sodium, calcium, and magnesium chlorides deposited on zinc and carbon steel surfaces was studied under atmospheric conditions. The cations strongly affected the corrosion rate of zinc, whereas they had a significantly lower impact on the corrosion of carbon steel. The corrosivity of cations of chloride salts for zinc increased in order of Mg2+ < Ca2+ < Na+. The higher corrosion resistance of zinc treated with calcium and magnesium chlorides was connected to prevention of formation of hydrozincite during zinc exposure in wet air. It was observed that zinc weight loss and the carbonate to simonkolleite ratio in corrosion products were correlating. The principal protective effect of bivalent cations can be seen in the decrease of pH of the surface electrolyte, which was caused by hydrolysis of such cations and subsequent formation of simonkolleite that blocked the cathodic sites.

sted, utgiver, år, opplag, sider

2007. Vol. 49, nr 6, s. 2676-2693

Emneord [en]

A. Zinc, B. IR spectroscopy, C. Atmospheric corrosion, Steel, Weight loss, Corrosion resistance, Electrolytes, Infrared spectroscopy, pH effects, Zinc, Chloride salts, Hydrozincite, Atmospheric corrosion

HSV kategori

Identifikatorer

URN: urn:nbn:se:ri:diva-40433DOI: 10.1016/j.corsci.2006.11.004Scopus ID: 2-s2.0-34047273902OAI: oai:DiVA.org:ri-40433DiVA, id: diva2:1361290

Merknad

We gratefully acknowledge financial support and help of all members of the project task force: Mika Hautala (Ruukki), Fabrice Tinardon (SNCZ), Per-Erik Augustsson (SSAB), Rémy Hellouin and Martin Jourdier (Arcelor Research), Dave Francis (AkzoNobel), Michel Belladone (Sigma Coatings), Igor Flis and Bengt Ingman (Becker Industrial Coatings), and Fernando Actis (Siderar). Dan Persson of KIMAB and Mats Ström of VOLVO Car Corporation are specially thanked for valuable discussions. The authors thank Farid Samie of KIMAB, Cécile Hall of Institut de la Corrosion, and Ted Rönnevall of Metrohm Nordic AB for their experimental support.

Tilgjengelig fra: 2019-10-15 Laget: 2019-10-15 Sist oppdatert: 2023-11-01bibliografisk kontrollert

Open Access i DiVA

Fulltekst mangler i DiVA

Andre lenker

Forlagets fulltekstScopus

Person

Thierry, DominiqueTaxén, Claes

Søk i DiVA

Av forfatter/redaktør

Thierry, DominiqueTaxén, Claes

Av organisasjonen

I samme tidsskrift

Corrosion Science

Om emnet

Søk utenfor DiVA

GoogleGoogle ScholarTotalt: 109 treff