The local structures of Cu(I) and Cu(II) in (20-x)Na₂O-xK₂O-10CaO-70SiO₂ glasses with a copper content of 0.4 mol% have been investigated by Cu K-edge extended X-ray absorption fine structure (EXAFS) and X-ray absorption near edge structure (XANES). Complementary data for Cu(II) was derived using UV–Vis-NIR spectroscopy. Indication for mainly linear two-fold coordination of the Cu⁺ ion was found by both EXAFS and XANES, but other coordination between Cu⁺ and O^2– cannot be excluded. The Cu(I)-O bond lengths were found to be 1.79–1.83 ± 0.02 Å. EXAFS results showed that Cu(II) was mostly present in a Jahn-Teller distorted environment with oxygen, an octahedron with four shorter Cu(II)-O bonds and two longer in axial position. The equatorial bond lengths were found to be 1.89–1.91 ± 0.02 Å and the axial 2.20–2.24 ± 0.02 Å with no effect of the Jahn-Teller distortion of the octahedron when the glass composition was altered.